Facile surface glycosylation of PVDF microporous membrane via direct surface-initiated AGET ATRP and improvement of antifouling property and biocompatibility
This paper describes a facile and novel approach for the surface glycosylation of poly(vinylidene difluoride) (PVDF) microporous membrane. A glycopolymer poly(D-gluconamidoethyl methacrylate) (PGAMA) was tethered onto the membrane surface via activators generated by electron transfer atom transfer radical polymerization (AGET ATRP) directly initiated from the PVDF surface. Chemical changes of membrane surface were characterized by Fourier transform infrared spectroscopy (FTIR) and X-ray photoelectron spectroscopy (XPS). It was revealed that PGAMA was successfully grafted onto the membrane surface and its grafting density can be modulated in a wide range up to 2.4 mu mol/cm(2). The effects of glycosylation on membrane morphology, flux and surface hydrophilicity were investigated. Field emission scanning electron microscopy (FESEM) results indicated shrinkage of the surface pore diameters and the growth of the glycopolymer layer on the membrane surface. The static water contact angle (WCA) of the membrane surface decreased from 110 degrees to 30.4 degrees with the increase of grafting density, indicating that the PGAMA grafts dramatically improved the surface hydrophilicity. The protein adsorption and platelets adhesion experiments indicated that the grafted PGAMA could effectively improve the membrane antifouling property and biocompatibility. (C) 2011 Elsevier B.V. All rights reserved.