Applied Surface Science, Vol.257, No.11, 4836-4843, 2011
Synthesis and characterization of nanostructured Ag on porous titania
In this work, porous titania was prepared on bulk Ti by chemical oxidation, and then nanostructured silver (Ag) was deposited on titania surface by ion beam sputtering. After annealing treatment, Ag/TiO2 composites were characterized using X-ray photoelectron spectroscopy (XPS), scanning electron microscopy (SEM) and transmission electron microscopy (TEM). Results indicated that a nano-porous titania layer with mean pore size of 150nm and thickness of 1 mu m was formed by chemical oxidation at 80 degrees C for 45 min. There were three Ag species (Ag (0), Ag (1+), and Ag (2+)) on composites surface after annealing treatment, and metallic Ag content achieved maximum value with annealing temperature of 500 degrees C in air. Ag showed high thermal stability being partly attributed to the inhibiting the diffusion of Ag by the underlying porous titania. (c) 2010 Elsevier B.V. All rights reserved.