Applied Surface Science, Vol.256, No.8, 2440-2446, 2010
Two component silicone modified epoxy foul release coatings: Effect of modulus, surface energy and surface restructuring on pseudobarnacle and macrofouling behavior
Two component silicone modified epoxy resin based low surface energy and non-toxic foul release coatings were developed. Silicone modified epoxy resin with 15 and 30% silicone content was used as component A and a polyether diamine (Jeffamine-500) was used as the component B. Free standing films were prepared by casting a mixture of components A and B in stoichiometric proportions. The surface composition, surface topography and wetting properties of the coatings were studied by angle resolved X-ray photoelectron spectroscopy (XPS), atomic force microscopy (AFM) and contact angle goniometry respectively. The mechanical properties of the cured films were evaluated by tensile measurements as well as dynamic mechanical analysis. Pseudobarnacles made of aluminium studs were attached to the coated panels and adhesion tests were carried out by a pseudobarnacle tester. Coated panels were exposed in Mumbai harbor for fouling studies for a period of 90 days. Surface restructuring studies of the coatings upon immersion in seawater were carried out by measuring the changes in advancing and receding contact angles by contact angle goniometry. The effect of surface energy, modulus and surface restructuring of the coatings on the macrofouling and pseudobarnacle adhesion properties has been discussed in detail. (C) 2009 Elsevier B. V. All rights reserved.