Journal of Power Sources, Vol.193, No.2, 541-546, 2009
Quaternized cardo polyetherketone anion exchange membrane for direct methanol alkaline fuel cells
Quaternized cardo polyetherketone (QPEK-C) membranes for alkaline fuel cells were prepared via chloromethylation, quaternization and alkalization of cardo polyetherketone (PEK-C). The chemical reaction for PEK-C modification was confirmed by nuclear magnetic resonance (H-1 NMR) and energy-dispersive X-ray spectroscopy (EDAX). The QPEK-C membrane was characterized by X-ray photoelectron spectroscopy (XPS) and thermo gravimetric analysis (TG). The ion-exchange content (IEC), water and methanol uptakes, methanol permeability and conductivity of the QPEK-C membranes were measured to evaluate their applicability in alkaline methanol fuel cells. The ionic conductivity of the QPEK-C membrane varied from (1.6 to 5.1) x 10(-3) S cm(-2) over the temperature range 20-60 degrees C. The QPEK-C membrane showed excellent methanol resistance. When the concentration of methanol was 4 M, the methanol permeability was less than 10(-9) cm(2) s(-1) at 30 degrees C. (c) 2009 Elsevier B.V. All rights reserved.