Journal of Polymer Science Part A: Polymer Chemistry, Vol.46, No.13, 4451-4458, 2008
Regio-regular structure high molecular weight poly(propylene carbonate) by rare earth ternary catalyst and Lewis base cocatalyst
Lewis base modification strategy on rare earth ternary catalyst was disclosed to enhance nucleophilic ability of active center during copolymerization of carbon dioxide and propylene oxide (PO), poly(propylene carbonate) (PPC) with H-T linkages over 83%, and number-average molecular weight (M-n) up to 100 kg/mol was synthesized at room temperature using Y(CCl3OO)(3)-ZnEt2-glycerine catalyst and 1,10-phenanthroline (PHEN) cocatalyst. Coordination of PHEN with active Zinc center enhanced the nucleophilic ability of the metal carbonate, which became more regio-specific in attacking carbon in PO, leading to PPC with improved H-T linkages. Moreover, the binding of PHEN to active Zinc center also raised the carbonate content of PPC to over 99%, whereas the PPC from common rare earth ternary catalyst was about 96%. Unlike the highly regio-regular structure PPC but with relatively low molecular weight recently reported in the literature, our high molecular weight regio-regular PPC did show significant improvement in thermal and mechanical performances. PPC with H-T linkages up to 83.2% showed glass transition temperature (T-g) of 43.3 degrees C, while T-g of PPC with H-T linkages of 69.7% was only 36.1 degrees C. When H-T connectivity was raised from 69.7 to 83.2%, the modulus of PPC showed a 78% increase. (c) 2008 Wiley Periodicals, Inc.