Nonisothermal crystallization kinetics of poly(vinylidene fluoride) in a poly(vinylidene fluoride)/dibutyl phthalate/di(2-ethylhexyl)phthalate system phase separation
The nonisothermal crystallization kinetics of poly(vinylidene fluoride) (PVDF) in PVDF/dibutyl phthalate (DBP)/di(2-ethylhexyl)phthalate (DEHP) blends via thermally induced phase separation were investigated through differential scanning calorimetry measurements. The Ozawa approach failed to describe the crystallization behavior of PVDF in PVDF/DBP/DEHP blends, whereas the modified Avrami equation successfully described the nonisothermal crystallization process of PVDF. Two stages of crystallization were observed in this analysis, including primary crystallization and secondary crystallization. The influence of the cooling rate and DBP ratio in the diluent mixture on the crystallization mechanism and crystal structure was determined by this method. The Mo approach well explained the kinetics of primary crystallization. An analysis of these two methods indicated that the increase in the DBP ratio in the diluent mixture caused a decrease in the crystallization rate at the primary crystallization stage. The activation energy was determined according to the Kissinger method and also decreased with the DBP ratio in the diluent mixture increasing. (c) 2007 Wiley Periodicals, Inc.