Journal of Physical Chemistry B, Vol.111, No.26, 7497-7500, 2007
Structural and ferromagnetic properties of epitaxial SrRuO3 thin films obtained by polymer-assisted deposition
Epitaxial ferromagnetic SrRuO3 thin films with a room-temperature resistivity of 300 mu Omega center dot cm have been successfully grown on LaAlO3(001) substrates at a processing temperature in the range of 550-750 degrees C by a polymer-assisted deposition technique. X-ray diffraction analysis shows good epitaxial quality of SrRuO3 thin films, giving values of the full width at half-maximum (FWHM) of 0.42 degrees from the rocking curve for the (002) reflection and 1.1 degrees from the in-plane phi scan for the (204) reflection. Both the resistivity and the magnetization versus temperature measurements show that the SrRuO3 films are ferromagnetic with a transition temperature of 160 K. The spontaneous magnetization near the ferromagnetic transition follows the scaling law, and the low-temperature magnetization follows the Bloch law.