Applied Surface Science, Vol.252, No.4, 1175-1181, 2005
Characterization of bilayer coatings of TiN/ZrN grown using pulsed arc PAPVD
Nitride coatings have been used to increase hardness and to improve the wear and corrosion resistance of structural materials. Coatings of TiN/ZrN were grown on stainless steel substrates using a physical vapour deposition system assisted by pulsed arc plasma (PAPVD). The coatings have been characterized by X-ray diffraction (XRD) in order to identify the present phases of the films, microstrain level generated, crystallite size and the variation of the lattice parameter. The results showed plane orientations (1 1 1) and (2 0 0) in both TiN and ZrN films. Morphology surface analysis of the samples were performed using a scanning probe microscope to characterize the grain size and roughness in the mode of the atomic force microscopy (AFM) hence it was observed that the root-mean-squared (rms) roughness for ZrN is smaller than for TiN. Besides elastic and friction properties of the films were characterized qualitatively, and then, they were compared with those of the substrates by using force modulation microscopy (FMM) and lateral force microscopy (LFM) modes. In addition, an elemental analysis of the samples was realized by means of energy dispersive spectroscopy (EDS). Both, XRD and AFM results are given as a function of the number of shots. Chemical states of the TiN and ZrN films were determined by X-ray photoelectron spectroscopy (XPS). (c) 2005 Published by Elsevier B.V.