Evolution of oxidation states in vanadium-based catalysts under conventional XPS conditions
The stability of different vanadium-based catalysts for the selective oxidation of small hydrocarbons under the ultra-high vacuum (UHV) conditions of standard X-ray photoelectron spectroscopy (XPS) was studied by using a multi-purpose surface analysis apparatus which allows time spans of only a few minutes between the sample transfer into vacuum and the first photoelectron spectrum. For vanadium phosphorus oxide catalysts a significant dependence of the average vanadium oxidation state on the time of exposure to the UHV was observed, with a substantial decrease of the V+5/V+4 ratio within only a few minutes. A much less pronounced reduction was found for alumina-supported VOx, catalysts. The observed changes are predominantly due to the vacuum environment with a rather minor (if at all) contribution of the X-ray excitation. (c) 2004 Elsevier B.V. All rights reserved.