Macromolecules, Vol.38, No.4, 1172-1179, 2005
Functionalization of single-walled carbon nanotubes with well-defined polymers by radical coupling
Polystyrene and poly[(tert-butyl acrylate)-b-styrene] with well-defined molecular weights and polydispersities were prepared by nitroxide-mediated free-radical polymerization. The homopolymers and block copolymers were used to functionalize shortened single-walled carbon nanotubes (SWNTs) through a radical coupling reaction involving polymer-centered radicals generated at 125degreesC via loss of the stable free-radical nitroxide capping agent. The resulting polymer-SWNT composites were fully characterized and were found to be highly soluble in a variety of organic solvents. This solubility could also be altered through chemical modification of the appended polymers. The tert-butyl groups of appended poly [(tert-butyl acrylate)-b-styrene] could be removed to produce poly[(acrylic acid)-b -styrene]-functionalized carbon nanotubes. The resulting composite was found to form aggregates in a mixture of chloroform/methanol (v/v: 1/1) as determined by dynamic light scattering.