폴리(에틸렌 글리콜) 디아크릴레이트/이온성 액체 젤형 고분자전해질의 제조 및 특성 연구
A Study on the Preparation and Characterization of Gel Polymer Electrolyte from Poly(ethylene glycol) Diacrylate in Ionic Liquid
E-mail:
초록
본 연구에서는 폴리(에틸렌 글리콜) 디아크릴레이트(PEGDA) 고분자 매트릭스에 이온성 액체인 1-butyl-3-methyl-imidazolium bis((trifluoromethyl) sulfonyl) amide(BuMeIm+Tf2N-)로 구성된 전해질 용액을 함유하는 젤 형태의 고분자 전해질을 제조하였다. 이온성 액체가 고분자 전해질의 이온 전도도에 미치는 영향을 조사하였으며, 기존의 유기 용매를 넣은 고분자 전해질보다 높은 이온 전도도(ca. 10-3S/cm)와 전기 화학적 안정성을 나타냄을 알 수 있었다.
A new type of polymer gel electrolyte was prepared from poly(ethylene glycol) diacrylate(PEGDA) and 1-butyl-3-methylimidazolium bis((trifluoromethyl) sulfonyl) amide(BuMeIm+Tf2N-) ionic liquid. The effect of the ionic liquid on ionic conductivity of the gel polymer electrolyte was investigated. It was observed that the gel polymer electrolyte having the ionic liquid exhibited higher ionic conductivity (ca. 10-3S/cm) as well as electrochemical stability than that using organic solvent.
  1. Murata K, Izuchi S, Yoshihisa Y, Electrochim. Acta, 45(8-9), 1501 (2000) 
  2. Voice AM, Southall JP, Rogers V, Matthews KH, Davies GR, Mcintyre JE, Ward IM, Polymer, 35(16), 3363 (1994) 
  3. Abraham KM, Alamgir M, J. Power Sources, 43, 195 (1993) 
  4. Kono M, Nishiura M, Ishiko E, J. Power Sources, 81, 748 (1999) 
  5. Kono M, Nishiura M, Ishiko E, Sada T, Electrochim. Acta, 45(8-9), 1307 (2000) 
  6. Alamgir M, Abraham KM, J. Electrochem. Soc., 140, L96 (1993) 
  7. Kang Y, Lee C, Polym. Sci. Technol., 14(4), 396 (2003)
  8. Jung HR, Cho MS, Ahn JH, Nam JD, Lee Y, J. Appl. Polym. Sci., 91(2), 894 (2004) 
  9. Cho MS, Shin B, Nam JD, Lee Y, Song K, Polym. Int., 53, 1523 (2004) 
  10. Cho MS, Shin B, Choi SD, Lee Y, Song KG, Electrochim. Acta, 50, 331 (2004) 
  11. Pyati R, Murray RW, J. Electrochem. Soc., 143(2), 401 (1996) 
  12. Watanabe M, Mizumura T, Solid State Ion., 86, 353 (1996) 
  13. Noda A, Watanabe M, Electrochim. Acta, 45(8-9), 1265 (2000) 
  14. Sun J, MacFarlane DR, Forsyth M, Solid State Ion., 147(3-4), 333 (2002) 
  15. Welton T, Chem. Rev., 99(8), 2071 (1999) 
  16. Davis JH, Fox PA, Chem. Commun., 11, 1209 (2003) 
  17. Seddon KR, Chem. Commun., 19, 2097 (1998) 
  18. Lagrost C, Carrie D, Vaultier M, Hapiot P, J. Phys. Chem. A, 107(5), 745 (2003) 
  19. Schroder U, Compton RG, Marken F, Bull SD, Davies SG, Gilmour S, J. Phys. Chem. B, 105(7), 1344 (2001) 
  20. Quinn BM, Ding ZF, Moulton R, Bard AJ, Langmuir, 18(5), 1734 (2002) 
  21. Bonhote P, Dias AP, Papageorgiou N, Kalyanasundaram K, Gratzel M, Inorg. Chem., 35(5), 1168 (1996) 
  22. Tiyapiboonchaiya C, MacFarlane DR, Sun J, Forsyth M, Macromol. Chem. Phys., 203, 1906 (2002) 
  23. Fuller J, Breda AC, Carlin RT, J. Electroanal. Chem., 459(1), 29 (1998) 
  24. Kim J, Moon S, Jin B, Gu H, Yun M, J. of KIEEME(in Korean), 8, 487 (1995)
  25. Shin JH, Henderson WA, Passerini S, Electrochem. Commun., 5, 1016 (2003) 
  26. MacFarlane DR, Huang J, Forsyth M, Nature, 402, 792 (1999) 
  27. Rajendran S, Sivakumar M, Subadevi R, Mater. Lett., 58, 641 (2004)