Macromolecular Research, Vol.12, No.4, 399-406, August, 2004
Structural and Property Changes in Glass-like Carbons Formed by Heat Treatment and Addition of Filler
E-mail:
Glass-like carbon precursors shrink significantly during curing and carbonization, which leads to crack formation and bending. Cured furan resin powder and ethanol were added to furan resin to diminish the weight loss, to suppress the shrinkage and bending, and to readily release the gases evolved during polymerization and curing. Curing and carbonization were controlled by pressure and slow heating to avoid damage to the samples. The effect of the filler and ethanol on the fabrication process was examined by measuring the properties of the glass-like carbon, such as the specific gravity, bending strength, electrical resistivity, and microstructural change. The specific gravities of the filler-added glass-like carbons were higher than those of the ethanol-added samples because of the formation of macropores from the vaporization of ethanol during the curing and polymerization processes. Although the ethanol-added glass-like carbons exhibited lower bending strengths after carbonization than did the filler-added samples, the opposite result was observed after aging at 2,600 ℃. We found that the macropores created from ethanol were contracted and removed upon heat treatment. The electrical resistivity of the glass-like carbon aged at 2,600 ℃ was lower than those of the samples carbonized at 1,000 ℃. We attribute this phenomenon to the fact that aging at high temperature led to well-developed microstructures, the removal of macropores, and the reduction of the surface area.
  1. Fitzer EW, Schaffer W, Yamada S, Carbon, 7, 643 (1969) 
  2. Constant KP, Lee JR, Chiang YM, J. Mater. Res., 11, 2338 (1996)
  3. Nakamizo M, Carbon, 29, 757 (1991) 
  4. Fishbach DB, Rorabaugh ME, Carbon, 21, 429 (1983) 
  5. Fukuyama K, Nishizawa T, Nishikawa K, Carbon, 39, 1863 (2001) 
  6. Rousseaux F, Tchoubar D, Carbon, 15, 63 (1997) 
  7. Honda H, Kobayashi K, Sugawara S, Carbon, 6, 571 (1968) 
  8. Saxena RR, Bragg RH, Carbon, 16, 373 (1978) 
  9. Park SM, Yasuda E, Akatsu T, Tanabe Y, Kakihana M, Ozawa K, Carbon, 33, 1377 (1995) 
  10. Kaae JL, Carbon, 23, 39 (1985) 
  11. Botelho EC, Scherbakoff N, Rezende MC, Carbon, 39, 45 (2001) 
  12. Fischbach DB, Carbon, 9, 193 (1971) 
  13. Gary WJ, Morgan WC, Cox JH, Woodruff EM, Carbon, 10, 236 (1972) 
  14. Fukuyama K, Nishizawa T, Nishikawa K, Carbon, 39, 2017 (2001) 
  15. Zhao JX, Bradt RC, Walker PL, Carbon, 23, 15 (1985) 
  16. Yoshida A, Kaburagi Y, Hishiyama Y, Carbon, 29, 1107 (1991) 
  17. Siebeneck HJ, Urick PA, Hasselman DPH, Minford EJ, Bradt RC, Carbon, 15, 187 (1977) 
  18. Lausevic Z, Jenkins GM, Carbon, 24, 651 (1986) 
  19. Shindo A, Izumino K, Carbon, 32, 1233 (1994) 
  20. Kyotani T, Yamada H, Sonobe N, Tomita A, Carbon, 32, 627 (1994) 
  21. Oya A, Marsh H, Heintz EA, Rodriguez-Reinoso F, (Eds.), Introduction to Carbon Technologies, Universidad de Alicante, Secretariado de Publicaciones, 561 (1997)
  22. Lim YS, Kim HS, Kim MS, Cho NH, Nahm S, Macromol. Res., 11(2), 122 (2003)
  23. Bose S, Bragg RH, Carbon, 19, 289 (1981)