Journal of Colloid and Interface Science, Vol.246, No.1, 122-128, 2002
Luminescent properties of tris(2,2'-bipyridine)ruthenium(II) in sol-gel-processed dip-coated thin films
The luminescence decay and spectral behavior of ruthenium(II)-tris-1,2-bipyridine dichloride dissolved in different organically modified silicate gel matrixes were investigated. Dip-coated thin films were synthesized from tetraetboxysilane (TEOS), methyltriethoxysilane (MTEOS), ethyltriethoxysilane (ETEOS), and methyltrimethoxysilane (MTMOS). A blue shift in the ruthenium complex emission spectrum with respect to the aqueous solution was observed for all the films on the Sol to gel conversion. This spectral shift was slightly dependent on the precursor used to obtain the films and independent of the reaction pH to prepare the "sol". In the data treatment of the time-resolved luminescence measurements, it was assumed that the distribution of the luminophore in the films was nonhomogeneous. The analysis of the luminescence decay profiles was based on a multisite model. All decay curves are best described by a double-exponential model. The parameters of the decay components depended principally on the thermal treatment used in the processing of the films. The lifetimes decreased and the emission espectra showed a red shift with the increase in the drying temperature. A luminescence quenching of the ruthenium complex in the films by dissolved oxygen in aqueous solution was also observed. The quenching rate constant obtained from the preexponential amplitude-weighted mean lifetimes (tau(M)) was in the order of 10(9) M-1 s(-1). When a phenolic derivative was used as quencher the process rate was greatly reduced compared to the quenching in water. It would seem that the metallic complex sequestered within the film, is placed either into a higher microviscosity microenvironment or in a location which the phenolic quencher cannot access. In both cases, the quenching plot based on tau(M)(0)/tau(M) could be fitted satisfactorily by a sum of two terms of Stern-Volmer. This fact is indicative of the matrix microheterogeneity for the films and is fully consistent with the biexponential nature of the luminescence intensity decay profiles.