Journal of Polymer Science Part B: Polymer Physics, Vol.40, No.3, 272-283, 2002
Mechanical properties of clay-reinforced polyamide
Intercalated and exfoliated nanocomposites were prepared by extrusion and injection of polyamide-6 and highly swollen or slightly swollen montmorillonite, respectively. The microstructure of the nanocomposites has been studied previously. In this article, we investigated the influence of the preferential orientation of the montmorillonite sheets on the mechanical properties of the nanocomposites. Dynamic mechanical analysis and tensile tests showed that the elastic modulus depends mainly on the filler loading. A parallel coupling could well account for the behavior of the nanocomposites. The calculated elastic and storage moduli of montmorillonite were set to 140 and 40 GPa, respectively. Compression tests were performed to study the anisotropy of the mechanical properties. The elastic modulus and flow strain were sensitive to the filler orientation. A Tandon-Weng approach was applied to consider the geometry of the filler. In all low-deformation tests, no significant difference between intercalated and exfoliated systems was observed. Finally, the influence of the dispersion and exfoliation state of the filler on the ultimate properties of the nanocomposites (tensile tests) is discussed.