MIL-88A (Fe) filler with duplicate corrosion inhibitive/barrier effect for epoxy coatings: Electrochemical, molecular simulation, and cathodic delamination studies
E-mail:,
The MIL-88A (Fe) as a MOF based on Fe+3 cations and fumaric acid was fabricated as a corrosion inhibitive filler to achieve a protective coating with duplicate active/passive inhibition properties. The polarization test indicated that the MIL-88A (Fe) saline-based extract had an inhibition effect. The formation of an inhibitive layer was seen in the EIS results for the sample immersed in the MIL-88A (Fe) extract. The slight solubility of MIL-88A (Fe) in the water (122.4 ppm total organic carbon and 2 ppm Fe+3) caused the inhibitive ions' release. The adsorption of release species from MIL-88A (Fe) scaffold on the substrate was confirmed by the theoretical (QM, MC/MD) computations. The EIS and salt spray test results obtained from scratched epoxy coated samples showed the Epoxy-MIL-88A (Fe) coating's active inhibition effect. The pull-off adhesion strength and cathodic delamination resistance were also improved in the presence of MIL-88A (Fe). The adhesion loss of epoxy coatings after 7 days of exposure to the salt spray decreased from 31.4% to 9.4%, respectively. The unscratched samples filled with MIL-88A (Fe) particles showed excellent barrier properties. The breakpoint frequency value declined from 2.4 to 0.8, and the reduction of low-frequency impedance magnitude decreased from 33% to 20%.
  1. Morozov Y, Calado L, Shakoor R, Raj R, Kahraman R, Taryba M, Montemor M, Corrosion Sci., 159, 108128 (2019)
  2. Raj R, Morozov Y, Calado LM, Taryba MG, Kahraman R, Shakoor A, Montemor MF, Electrochim. Acta, 319, 801 (2019)
  3. Ramezanzadeh M, Bahlakeh G, Ramezanzadeh B, J. Mol. Liq., 290, 111212 (2019)
  4. Ralkhal S, Ramezanzadeh B, Shahrabi T, J. Alloy. Compd., 790, 141 (2019)
  5. Shi X, Nguyen TA, Suo Z, Liu Y, Avci R, Surf. Coat. Technol., 204, 237 (2009)
  6. Zhang Y, Zhao M, Zhang J, Shao Q, Li J, Li H, Lin B, Yu M, Chen S, Guo Z, J. Polym. Res., 25, 130 (2018)
  7. Hao Y, Liu F, Han EH, Anjum S, Xu G, Corrosion Sci., 69, 77 (2013)
  8. Azadi M, Heragh MF, Bidi MA, Prog. Color, Colorants Coatings 13, 213 (2020).
  9. Butova VV, Soldatov MA, Guda AA, Lomachenko KA, Lamberti C, Russ. Chem. Rev., 85, 280 (2016)
  10. Furukawa H, Cordova KE, O’Keeffe M, Yaghi OM, Science, 341, 123044 (2013)
  11. Silva P, Vilela SM, Tome JP, Paz FAA, Chem. Soc. Rev., 44, 6774 (2015)
  12. Choudhary H, Kumar R, Pawar S, Bose AAVS, Sahoo DS, Chem. Select, 3, 2120 (2018)
  13. Choudhary H, Kumar R, Pawar S, Sundararaj U, Sahoo DB, Phys. Chem. Chem. Phys., 21, 15595 (2019)
  14. Choudhary HK, Kumar R, Pawar SP, Sundararaj U, Sahoo B, Carbon, 164, 357 (2020)
  15. Kumar R, Kumar A, Verma N, Philip R, Sahoo B, J. Alloy. Compd., 849, 156665 (2020)
  16. Kumar R, Kumaran AAVV, Sahoo DB, Nano-Struct. Nano-Objects, 16, 167 (2018)
  17. Kumar R, Kumar A, Verma N, Khopkar V, Philip R, Sahoo B, ACS Appl. Nano Mater., 3, 8618 (2020)
  18. Levine K, Sahoo DB, Smart Nanocomposites, 5, 1 (2014)
  19. Mesbah A, Juers C, Lacouture F, Mathieu S, Rocca E, Francois M, Steinmetz J, Solid State Sci., 9, 322 (2007)
  20. Mesbah A, Jacques S, Rocca E, Francois M, Steinmetz J, Eur. J. Inorg. Chem., 2011, 1315 (2011)
  21. Wu C, Liu Q, Chen R, Liu J, Zhang H, Li R, Takahashi K, Liu P, Wang J, ACS Appl. Mater. Interfaces, 9, 11106 (2017)
  22. Zhang M, Ma L, Wang L, Sun Y, Liu Y, ACS Appl. Mater. Interfaces, 10, 2259 (2018)
  23. Liu W, Yan Z, Ma X, Geng T, Wu H, Li Z, Materials, 11, 396 (2018)
  24. Etaiw SEDH, Fouda AEAS, Abdou SN, El-bendary MM, Corrosion Sci., 53, 3657 (2011)
  25. Fouda AEAS, Etaiw SEDH, El-bendary MM, Maher MM, J. Mol. Liq., 213, 228 (2016)
  26. Tian H, Li W, Liu A, Gao X, Han P, Ding R, Yang C, Wang D, Corrosion Sci., 131, 1 (2018)
  27. Zafari S, Shahrak MN, Ghahramaninezhad M, Metals Mater. Int., 26, 25 (2020)
  28. Kumaraguru S, Pavulraj R, Mohan S, Trans. IMF, 95, 131 (2017)
  29. Zheng Q, Li J, Yuan W, Liu X, Tan L, Zheng Y, Yeung KWK, Wu S, ACS Sustain. Chem. Eng., 7, 18114 (2019)
  30. Guo Y, Wang J, Zhang D, Qi T, Li GL, Colloids Surf. A: Physicochem. Eng. Asp., 561, 1 (2019)
  31. Motamedi M, Ramezanzadeh M, Ramezanzadeh B, Mahdavian M, Chem. Eng. J., 382, 122820 (2020)
  32. Xiong L, Liu J, Yu M, Li S, Corrosion Sci., 146, 70 (2019)
  33. Ramezanzadeh M, Ramezanzadeh B, Mahdavian M, Bahlakeh G, Carbon, 161, 231 (2020)
  34. Tarzanagh YJ, Seifzadeh D, Rajabalizadeh Z, Habibi-Yangjeh A, Khodayari A, Sohrabnezhad S, Surf. Coat. Technol., 380, 125038 (2019)
  35. Lashgari SM, Yari H, Mahdavian M, Ramezanzadeh B, Bahlakeh G, Ramezanzadeh M, Corrosion Sci., 178, 109099 (2021)
  36. Surble S, Serre C, Mellot-Draznieks C, Millange F, Ferey G, Chem. Commun., 284 (2006).
  37. Ramsahye NA, Trung TK, Scott L, Nouar F, Devic T, Horcajada P, Magnier E, David O, Serre C, Trens P, Chem. Mater., 25, 479 (2013)
  38. McKinlay A, Eubank J, Wuttke S, Xiao B, Wheatley P, Bazin P, Lavalley JC, Daturi M, Vimont A, De Weireld G, Chem. Mater., 25, 1592 (2013)
  39. Xu WT, Ma L, Ke F, Peng FM, Xu GS, Shen YH, Zhu JF, Qiu LG, Yuan YP, Dalton Trans., 43, 3792 (2014)
  40. Wu Y, Luo H, Wang H, RSC Adv., 4, 40435 (2014)
  41. Lin KYA, Chang HA, Hsu CJ, RSC Adv., 5, 32520 (2015)
  42. Wang J, Wan J, Ma Y, Wang Y, Pu M, Guan Z, RSC Adv., 6, 112502 (2016)
  43. Wang L, Zhang Y, Li X, Xie Y, He J, Yu J, Song Y, Sci. Rep., 5, 1 (2015)
  44. Liu N, Huang WY, Zhang XD, Tang L, Wang L, Wang YX, Wu MH, Appl. Catal. B: Environ., 221, 119 (2018)
  45. Fu H, Song XX, Wu L, Zhao C, Wang P, Wang CC, Mater. Res. Bull., 125, 110806 (2020)
  46. Klamt A, Schuurmann G, A. J. Chem. Phys., 106, 6622 (1997)
  47. SD, Accelrys Software Inc., (2009).
  48. Saha SK, Ghosh P, Hens A, Murmu NC, Banerjee P, Phys. E: Low-dimensional Syst. Nanostruct., 66, 332 (2015).
  49. Saha SK, Murmu M, Murmu NC, Banerjee P, J. Mol. Liq., 224, 629 (2016)
  50. Olasunkanmi LO, Obot IB, Kabanda MM, Ebenso EE, J. Phys. Chem. C, 119, 16004 (2015)
  51. Verma C, Olasunkanmi LO, Ebenso EE, Quraishi MA, Obot IB, J. Phys. Chem. C, 120, 11598 (2016)
  52. Zhang T, Zhao N, Li J, Gong H, An T, Zhao F, Ma H, RSC Adv., 7, 23583 (2017)
  53. Hayatgheib Y, Ramezanzadeh B, Kardar P, Mahdavian M, Corrosion Sci., 133, 358 (2018)
  54. Zhang Z, Ba H, Wu Z, Zhu Y, Constr. Build. Mater., 198, 288 (2019)
  55. Derakhshan AA, Rajabi L, Karimnezhad H, Powder Technol., 225, 156 (2012)
  56. Bagherzadeh E, Zebarjad SM, Hosseini HRM, Eur. J. Inorg. Chem., 2018, 1909 (2018)
  57. Ibrahim M, Nada A, Kamal DE, Indian J. Pure Appl. Phys., 43, 911 (2005)
  58. Alexander S, Gomez V, Barron AR, J. Nanomater., 2016 (2016)
  59. Muryanto S, Sutanti S, Supriyo E, Putranto W, Effects of Malonic Acid on Calcium Carbonate Crystalline Phases and Morphology, Atlantis Press, 2018.
  60. Alibakhshi E, Ghasemi E, Mahdavian M, J. Sol-Gel Sci. Technol., 72, 359 (2014)
  61. Boily JF, Seward TM, J. Solution Chem., 34, 1167 (2005)
  62. Griffiths J, Colour and Constitution of Organic Molecules, Academic press, 1976.
  63. Liao X, Wang F, Wang F, Cai Y, Yao Y, Teng BT, Hao Q, Shuxiang L, Appl. Catal. B: Environ., 259, 118064 (2019)
  64. Motamedi M, Ramezanzadeh B, Mahdavian M, J. Ind. Eng. Chem., 66, 116 (2018)
  65. Askari F, Ghasemi E, Ramezanzadeh B, Mahdavian M, Dyes Pigment., 190, 189 (2014)
  66. Sherif ES, Int. J. Electrochem. Sci., 6 (2011)
  67. Wang NG, Wang RC, Peng CQ, Yan F, Zhan XY, Trans. Nonferrous Met. Soc. China, 20, 1936 (2010)
  68. Salehi E, Naderi R, Ramezanzadeh B, Appl. Surf. Sci., 396, 1499 (2017)
  69. Yadav A, Kumar R, Sahoo B, ACS Appl. Nano Mater., 3, 3540 (2020)
  70. Yadav A, Kumar R, Pandey UP, Sahoo B, Carbon, 173, 350 (2021)
  71. Yadav A, Kumar R, Choudhary H, Sahoo DB, Carbon, 140, 477 (2018)
  72. Ramezanzadeh B, Vakili H, Amini R, J. Ind. Eng. Chem., 30, 225 (2015)
  73. Haddadi SA, Alibakhshi E, Bahlakeh G, Ramezanzadeh B, Mahdavian M, J. Mol. Liq., 284, 682 (2019)
  74. Orazem ME, Tribollet B, New Jersey, (2008).
  75. Hirschorn B, Orazem ME, Tribollet B, Vivier V, Frateur I, Musiani M, Electrochim. Acta, 55(21), 6218 (2010)
  76. Chen D, Yen M, Lin P, Groff S, Lampo R, McInerney M, Ryan J, Materials, 7, 5746 (2014)
  77. Akbarzadeh S, Ramezanzadeh M, Bahlakeh G, Ramezanzadeh B, J. Mol. Liq., 297, 111862 (2020)
  78. Akbarzadeh S, Ramezanzadeh B, Bahlakeh G, Ramezanzadeh M, J. Mol. Liq., 296, 111809 (2019)
  79. Kambhampati P, Child CM, Foster MC, Campion A, J. Chem. Phys., 108(12), 5013 (1998)
  80. Du Y, Fang H, Zhang Q, Zhang H, Hong Z, Spectroc. Acta Pt. B-Atom. Spectr., 153, 580 (2016)
  81. Chamritski I, Burns G, J. Phys. Chem. B, 109(11), 4965 (2005)
  82. Soler M, Qu F, Raman Spectroscopy of Iron Oxide Nanoparticles, PP.379 (2012).
  83. Ramezanzadeh M, Bahlakeh G, Sanaei Z, Ramezanzadeh B, Appl. Surf. Sci., 463, 1058 (2019)
  84. Musa AY, Jalgham RT, Mohamad AB, Corrosion Sci., 56, 176 (2012)
  85. Khaled KF, Electrochim. Acta, 55(22), 6523 (2010)
  86. Zhang J, Qiao G, Hu S, Yan Y, Ren Z, Yu L, Corrosion Sci., 53, 147 (2011)
  87. Sanaei Z, Ramezanzadeh B, Shahrabi T, Appl. Surf. Sci., 454, 1 (2018)
  88. Ramezanzadeh M, Bahlakeh G, Ramezanzadeh B, J. Alloy. Compd., 792, 375 (2019)
  89. Wan H, Song D, Ii X, Zhang D, Gao J, Du C, Materials, 10, 654 (2017)
  90. Asaldoust S, Hosseini MS, Ramezanzadeh B, Bahlakeh G, Constr. Build. Mater., 256, 119439 (2020)
  91. Javidparvar AA, Naderi R, Ramezanzadeh B, Compos. B: Eng., 172, 363 (2019)
  92. Abdou MI, El-Sayed Ahmed H, Gaber MAW, Fadl AM, Cogent Eng., 5, 142784 (2018)
  93. Ramezanzadeh B, Ghasemi E, Askari F, Mahdavian M, Dyes Pigment., 122, 331 (2015)
  94. Hamadi L, Mansouri S, Oulmi K, Kareche A, Egypt. J. Pet., 27, 1157 (2018)
  95. Samiee R, Ramezanzadeh B, Mahdavian M, Alibakhshi E, J. Clean Prod., 220, 340 (2019)