Solar Energy, Vol.217, 25-28, 2021
The low-temperature preparation for crystalline Sb2S3 thin films and photovoltaic performance of the corresponding solar cells
The crystalline Sb2S3 thin films with the preferential orientation of (020) were firstly prepared at the low pyrolysis-crystallization temperature of 200 degrees C using the mixture solution of Sb2O3, CS2, n-butylamine in ethanol or DMF as solvents. The influence of solvent ethanol and DMF on the morphology of the Sb2S3 thin films was compared and photovoltaic performance of the corresponding solar cells was evaluated. The power conversion efficiency of the Sb2S3 thin film solar cells achieved 5.00% for ethanol and 5.44% for DMF.