Macromolecular Research, Vol.29, No.4, 297-305, April, 2021
Adhesive Strength Between Metal Sheet Plated Using Micro Particles and ABS Resin
E-mail:
To improve the adhesive strength between metal and acrylonitrile butadiene styrene (ABS) resin, a metal surface was embossed with an irregular shape, and then we studied the bonding between different materials by insert molding. The irregular embossing of the metal surface was completed by nickel plating using micro particles of artificial diamond and aluminum oxide. Particles of various sizes were used, and the plating height was set at 1/2, 1/3, and 1/4 of the particle size. When the embossed surface was implemented on the metal surface through the particles, an undercut area was formed on the metal surface. During insert molding, the resin solidified in the undercut area, which increased the adhesive force. As the undercut size was different depending on the plating height and particle size, the adhesive strength varied, and as the particle size increased, the adhesive strength increased. The adhesion strength was higher in the plated specimens using aluminum oxide particles than those with artificial diamond particles. Moreover, the adhesive strength was better with ABS resin containing glass fiber than with pure ABS resin.
  1. Zhang Y, Zhu P, Chen G, Thin Walled Struct., 45, 670 (2007)
  2. Kastensson A, J. Clean Prod., 66, 337 (2014)
  3. Mahajan GV, Aher VS, IJSRP, 2, 1 (2012)
  4. Huang HX, Tian JD, Guan WS, Polym. Eng. Sci., 54(2), 327 (2014)
  5. Zhai WT, Kim YW, Jung DW, Park CB, Ind. Eng. Chem. Res., 50(9), 5523 (2011)
  6. Seo KH, Lim JC, Lim HS, Elastom. Compos., 35, 132 (2000)
  7. Stewart R, Reinf. Plast., 54, 22 (2010)
  8. Kim Y, Kil S, J. Weld. Join., 34, 31 (2016)
  9. Kim Y, Bang H, J. Weld. Join., 36, 27 (2018)
  10. Amancio ST, dos Santos JF, Polym. Eng. Sci., 49(8), 1461 (2009)
  11. Kim NH, Kim J, J. Adhes. Interface, 19, 173 (2018)
  12. Norman DA, Interactions, 9, 36 (2002)
  13. Kim SL, Lyu MY, Jang SW, Polym. Korea, 41(4), 727 (2017)
  14. Kim SL, Lyu MY, Polym. Eng. Sci., 59, E93 (2019)
  15. Potsch G, Michaeli W, in Injection Molding: An Introduction, Hanser, Munich, pp.180 2007.
  16. Honkanen M, Hoikkanen M, Vippola M, Vuorinen J, Lepisto T, J. Adhes. Sci. Technol., 23(13-14), 1747 (2009)
  17. Lho TJ, Kim JY, Kang DJ, Kim JH, Kim GY, J. KSPE, 25, 43 (2008)
  18. Zain NM, Ahmad SH, Ali ES, Int. J. Adhes. Adhes., 55, 43 (2014)
  19. Fabrin P, Hoikkanen M, Vuorinen J, in Proceedings of SPE Annual Technical Conference (ANTEC 2007), Cincinnati, OH, pp.2528 2007.
  20. Ghosh PK, Patel A, Kumar K, Polymer, 87, 159 (2016)
  21. Tahara M, Cuong NK, Nakashima Y, Surf. Coat. Technol., 173/174, 826 (2003)
  22. Prat R, Suwa T, Kogoma M, Okazaki S, J. Adhes., 66(1), 163 (1998)