International Journal of Hydrogen Energy, Vol.45, No.35, 17671-17684, 2020
Investigation of the hydrogen induced cracking behaviour of API 5L X65 pipeline steel
The effect of microstructural features on the hydrogen induced cracking (HIC) susceptibility of two API 5L X65 pipeline steels were investigated by cathodic charging, hydrogen permeation and hydrogen microprint experiments. Microstructural evaluation after hydrogen charging revealed cracks at the mid-thickness (segregation zone) of both plates. However, more severe cracks were observed in the plate with higher dislocation density and residual stresses. The plate with lower plastic strain and more {111}-oriented grains had less severe cracks. Inclusions found along the crack path, comprising of Si-enriched oxides and carbides contributed to the initiation and propagation of cracks. The variation of the trapping behaviour and hydrogen diffusion through the plates were examined. The results confirmed that a higher ratio of reversible to irreversible traps contributes to increasing HIC severity in steels. Additionally, hydrogen transport through the steels was most prominent along the grain boundaries, indicating the importance of grain boundary character to HIC. (C) 2020 Hydrogen Energy Publications LLC. Published by Elsevier Ltd. All rights reserved.