Advanced Powder Technology, Vol.31, No.2, 505-509, 2020
Synthesis of carbide solid solution with multiple components using elemental powder
Hf-Zr-Ti-C carbide was fabricated by free-pressureless spark plasma sintering and elemental powders. The synthesis temperature and oxygen content were 1600 degrees C and 0.6 wt%, respectively. There was no obvious impurity dissolving into the carbide powder due to avoiding the high-energy ball milling. The Hf-Zr-Ti-C carbide was a solid solution with FCC structure, and its lattice parameter was 0.463662 nm. This study provided a new method to synthesize the powder of carbide solid solution with multiple elements. (C) 2019 The Society of Powder Technology Japan. Published by Elsevier B.V. and The Society of Powder Technology Japan. All rights reserved.