Improvements of the Electrical Conductivity and EMI Shielding Efficiency for the Polycarbonate/ABS/Carbon Fiber Composites Prepared by Pultrusion Process
E-mail:
The electrical conductivity, electromagnetic interference (EMI) shielding efficiency, and the morphological and mechanical properties of the polycarbonate/poly(acrylonitrile-butadiene-styrene) (ABS) (70/30)/carbon fiber (CF) composites were studied. The composites were prepared by two different methods, i.e., the pultrusion process and screw extrusion. The composite prepared by the pultrusion process showed higher electrical conductivity of 1.05×101 S/cm and EMI shielding efficiency of 37.6 dB compared to the composite prepared by screw extrusion of 5.20×10-1 S/cm and 6.8 dB at 10 GHz. The increase in the shielding efficiency of electromagnetic wave by 30.8 dB was due to the increased fiber length when the composite was prepared by the pultrusion process. The tensile and flexural strengths of the polycarbonate/ABS (70/30)/CF composite prepared by the pultrusion process were slightly higher by 8.2 and 7.0% compared to those of the composites prepared by screw extrusion, respectively. The above results suggest that the pultrusion process is a superior method to prepare the polycarbonate/ABS (70/30)/CF composites with favorable electrical and mechanical properties.
  1. Choi EY, Nam JU, Hong SH, Kim CK, Macromol. Res., 26(2), 107 (2018)
  2. Ryu SC, Kim JY, Kim WN, J. Appl. Polym. Sci., 135, 46418 (2018)
  3. Chen T, Xue P, Jia M, Polym. Compos., 38, 157 (2017)
  4. Lee SH, Lee Y, Jang MG, Han C, Kim WN, J. Appl. Polym. Sci., 134, 45222 (2017)
  5. Lee SH, Kim JY, Koo CM, Kim WN, Macromol. Res., 25(9), 936 (2017)
  6. Jang MG, Ryu SC, Juhn KJ, Kim SK, Kim WN, J. Appl. Polym. Sci., 136, 47302 (2019)
  7. Chen J, Dong YJ, Jin FL, Park SJ, Macromol. Res., 27(1), 10 (2019)
  8. Hwang EB, Yoo TJ, Yu SJ, Jeon YG, Macromol. Res., 25(7), 697 (2017)
  9. Lee M, Koo J, Ki H, Lee KH, Min BH, Lee YC, Kim JH, Macromol. Res., 25(3), 231 (2017)
  10. King JA, Pisani WA, Klimek-McDonald DR, Perger WF, Odegard GM, Turpeinen DG, J. Compos. Mater., 50, 2177 (2016)
  11. Jang MG, Cho C, Kim WN, J. Compos. Mater., 51, 1005 (2017)
  12. Seyedi-Ghezghapan SM, Javadi A, Polym. Compos., 38, E269 (2017)
  13. Jang MG, Lee YK, Kim WN, Macromol. Res., 23(10), 916 (2015)
  14. Grinou A, Yun YS, Jin HJ, Macromol. Res., 20(1), 84 (2012)
  15. Maiti S, Khatus BB, Polym. Compos., 37, 2058 (2016)
  16. Markham D, Mater. Des., 21, 45 (2000)
  17. Al-Saleh MH, Saadeh WH, Sundararaj U, Carbon, 60, 146 (2013)
  18. Ott HW, in Electromagnetic Compatibility Engineering, Wiley, New York, Chap. 6, pp 238-265 2009.
  19. Al-Saleh MH, Sundararaj U, Carbon, 47, 1738 (2009)