Vapor-Phase Strategy to Pillaring of Two-Dimensional Zeolite
Two-dimensional (2D) layered zeolites are new forms of 3D zeolite frameworks. They can be pillared to form more open porous structures with increased access for reactants that are too big for the micropores of zeolites. The current pillaring procedure, however, requires intercalation of pillaring precursors by dispersing 2D zeolite in an alkoxide liquid and hydrolizing entrapped alkoxide to form inorganic oxide pillars in an aqueous alkaline solution. Both steps use excess solvents, generate significant waste, and require multiple synthesis and separation steps. Here we report a vapor-phase pillarization (VPP) process to produce pillared zeolites from 2D layered zeolite structures. The VPP process has similar to 100% efficiency of alkoxide usage in the intercalation step, requires less (and, in some cases, zero) water addition in the hydrolysis step, does not require separation for product recovery, and generates no liquid waste. Furthermore, synthesis of pillared zeolites via the VPP process can be accomplished within a single apparatus with one-time operation. The pillared zeolite prepared by the VPP method preserved the zeolitic layered structure as well as acidity and showed enhancement in catalytic alkylation of mesitylene with benzyl alcohol compared to 2D layered zeolite without pillarization treatment.