Competitive growth of Al2O3/YAG/ZrO2 eutectic ceramics during directional solidification: Effect of interfacial energy
The microstructure evolution and growth behavior of the Al2O3/Y3Al5O12(YAG)/ZrO2 ternary eutectic ceramics during directional solidification were well investigated. During directional solidification of the Al2O3/YAG/ZrO2 ternary eutectic ceramics, {1120} Al2O3 paralleled with {001}ZrO2 while they did not parallel with {001}YAG at the same time in the competitive growth stage. All of the interfaces parallel to each other finally. The area percentage of the Al2O3/ZrO2 and YAG/ZrO2 interfaces are 40.4 +/- 0.2% and 30.8 +/- 0.1%, respectively, higher than that of the Al2O3/YAG (28.8 +/- 0.2%). The content of Al2O3 and YAG phases are 39.9% and 41.1%, respectively, almost double of that of ZrO2. The interfaces of Al2O3/ZrO2 and YAG/ZrO2 are shorter and more dispersed than that of the Al2O3/YAG. It was found that the interfacial energy of Al2O3/ZrO2 and YAG/ZrO2 interfaces are lower than that of Al2O3/YAG. It can be concluded that interfacial energy plays a decisive role in affecting the crystallographic orientation and interfaces distribution in the Al2O3/YAG/ZrO2 eutectic since the interfaces of Al2O3/ZrO2 and YAG/ZrO2 with lower interfacial energy can be formed more easily during directional solidification. Therefore, the contents of Al2O3/ZrO2 and YAG/ZrO2 interfaces are higher. This study can provide theoretical guidance for interface design of multi-phase materials.