Reactive & Functional Polymers, Vol.127, 67-73, 2018
Poly(N,N-dimethylaminoethyl methacrylate) for removing chromium (VI) through polymer-enhanced ultrafiltration technique
This work is focused on the removal of Cr(VI) ions from aqueous solution using polymer-enhanced ultrafiltration (PEUF) techniques with water-soluble poly(N,N-dimethylaminoethyl methacrylate), PDMAEMA, used as sorbent. The polymer was prepared by reversible addition-fragmentation chain transfer (RAFT) polymerization at different reaction times, characterized by size exclusion chromatography (SEC) and proton nuclear magnetic resonance (H-1 NMR). The sorption of Cr(VI) was studied by PEUF as a function of pH, the polymer:Cr(VI) molar ratio, and the presence of interfering ions. The PEUF-enrichment mode was used to saturate the polymer and further determine the release of Cr(VI) and regeneration of the polymer using sorption-desorption process. The RAFT polymerization showed a yield in the range 46% to 79% (determined by H-1 NMR) for polymers with molecular weight (M-n) between 28 and 195 kg mol(-1). The polydispersity estimated by SEC was between 1.1 and 1.8. The capacity of PDMAEMA as sorbent of Cr(VI), by the PEUF technique showed an efficient removal of Cr(VI) (100%, 25 mg L-1 in the feed) at pH 4 using polymer:Cr molar ratio of 40:1. The presence of interfering ions does not significantly decrease the retention capacity of PDMAEMA. Finally the results indicated that PDMAEMA can release Cr(VI) and be regenerated.