Chinese Journal of Chemical Engineering, Vol.26, No.3, 642-647, 2018
Effects of nitrogen doping on surface-enhanced Raman scattering (SERS) performance of bicrystalline TiO2 nanofibres
In this work, we successfully synthesized bicrystalline anatase/TiO2(B) nanofibre and used it as active substrate for surface-enhanced Raman scattering (SERS) applications. The bicrystalline structured TiO2 substrates provide additional charge transfer across the anatase-TiO2(B) interface and thus enhanced activity compared to the pure single crystalline phase. With an effort to further increase the sensitivity of SERS, nitrogen element was doped into bicrystalline anatase/TiO2(B) nanofibres (N-TiO2) and higher SERS enhancementwas achieved. The nitrogen content was controlled by tuning the calcination temperature of titanate precursor at 500, 600 and 700 degrees C, respectively. The sample calcined at 600 degrees C (NT600) acquires the highest percentage of nitrogen element due to its open pore structure that facilitates the diffusion of nitrogen during calcination. Raman intensity depends on the amount of nitrogen doping, thus NT600 exhibited the best SERS activity. The doped nitrogen in TiO2 facilitates the charge transfer between TiO2 and probing molecules and thus suppresses the electron-hole recombination. This work provides a new perspective on the design of efficient TiO2 SERS active substrate and is expected to be valuable for adsorbate detection on semiconductor surface. (c) 2017 The Chemical Industry and Engineering Society of China, and Chemical Industry Press. All rights reserved.