Applied Surface Science, Vol.437, 329-335, 2018
Contact angle control of sessile drops on a tensioned web
In this study, the influence of the change of tension applied to flexible and thin web substrate on the contact angle of sessile drop in roll-to-roll system was investigated. Graphene oxide and deionized water solutions were used in the experiments. Tension was changed to 29, 49, and 69 N, and the casting distance of the micropipette and the material was set to 10, 20, and 40 mm, and the droplet volume was set to 10, 20, and 30 mu L, respectively. Statistical analysis of three variables and analysis of the variance methodology showed that the casting distance was most significant for the contact angle change, and the most interesting tension variable was also affected. The change in tension caused the maximum contact angle to change by 5.5 degrees. The tension was not uniform in the width direction. When the droplet was applied in the same direction in the width direction, it was confirmed that the tension unevenness had great influence on the contact angle up to 11 degrees. Finally, the casting distance, which has a large effect on the contact angle, was calibrated in the width direction to reduce the width direction contact angle deviation to 1%. This study can be applied to fine patterning research using continuous inkjet printing and aerosol jet printing, which are roll-to-roll processes based on droplet handling. (C) 2017 Elsevier B.V. All rights reserved.