Applied Surface Science, Vol.434, 514-521, 2018
Simple synthesis of nitrogen-rich polymer network and its further amination with PEI for CO2 adsorption
The nitrogen-rich polymer network (MF/PAM) was synthesized through interpenetration between the molecular chains of melamine-formaldehyde resin(MF) and polyacrylamide (PAM), to which the polyethylene imine (PEI) was grafted to obtain solid amine adsorbent (MF/PAM-g-PEI). Compared with MF, the swelling capacity of MF/PAM was greatly enhanced, it could swell rapidly and directly in water. Although the interpenetration of PAM into MF may reduce the porosity of MF/PAM, the CO2 capture capacity of the solid amine adsorbents (MF/PAM-g-PEI) could still reach 2.8 mmol/g at 273 K. The adsorbents also exhibited promising adsorption kinetics and regeneration performances. The kinetics observation showed that the Avrami model could better descript the CO2 adsorption process compared with the pseudo-first-order model and pseudo-second-order model. Meanwhile, the Avrami kinetic orders (n(a)) range from 1.21 to 1.56, displaying that the both physisorption and chemisorption exist in the adsorption process and the PEI have successfully grafted onto the polymer network, which also can be confirmed by the adsorption activation energy value. After 18 adsorption-desorption recycles, the MF/PAM-g-PEI could preserve its initial capacity without any decrease. Our work provides a new method to achieve promising solid amine adsorbents with higher adsorption capacity and better regeneration performance. (c) 2017 Elsevier B.V. All rights reserved.