Journal of Power Sources, Vol.364, 426-431, 2017
Highly efficient and thickness-tolerable bulk heterojunction polymer solar cells based on P3HT donor and a low-bandgap non-fullerene acceptor
In order to fabricate highly efficient polymer solar cells (PSCs) in industrial scale, one of the key issues is to use thick active layer (>200 nm) in the device module without sacrificing the power conversion efficiency (PCE). In this article, we have studied the blend of the medium-bandgap polymeric donor P3HT and the low-bandgap acceptor IDTIDT-IC as the active layer in non-fullerene PSCs, and successfully maintained the device performance with the thickness of the active layer close to 250 nm. The P3HT:IDTIDT-IC based PSCs with simple thermal annealing exhibits a PCE of 3.49% at a thin active layer, 74 nm. More importantly, the PCE remains almost constant with increasing the thickness of the active layer, and reaches a peak value of 3.64% at 236 nm. This thickness-insensitive photovoltaic performance of the P3HT:IDTIDT-IC system makes them compatible with large-scale roll-to-roll processing. Furthermore, the P3HT:IDTIDT-IC devices show a very high tolerance to temperature, and the PCE keeps nearly unchanged after annealing the active layer at 150 degrees C for 75 min. All in all, our results show that thickness-tolerable and thermal-stable P3HT:IDTIDT-IC system is more suitable for large-scale industrial manufacturing than the classic P3HT:PCBM formula. (C) 2017 Elsevier B.V. All rights reserved.