Electrochimica Acta, Vol.245, 705-714, 2017
Effect of diphenyl disulfide as an additive on the electrochemical performance of Li1.2Mn0.54Ni0.13Co0.13O2/graphite batteries at elevated temperature
The effect of diphenyl disulfide (DPDS) as a bifunctional additive on the performance of Li1.2Mn0.54Ni0.13Co0.13O2/graphite batteries cycled at elevated temperature was evaluated. The batteries with 1.0 wt.% DPDS exhibited a capacity retention of 68.4% after 100 cycles under 55 degrees C, which was higher than that without DPDS (44.4%). In addition, the self-discharge of the Li1.2Mn0.54Ni0.13Co0.13O2/graphite battery was also suppressed in a storage test at 85 degrees C for 8 h by adding 1.0 wt.% DPDS in the electrolyte. Linear sweep voltammetry and cyclic voltammetry combined with density functional theory calculations indicated that DPDS was oxidized and reduced prior to the solvent to participate in the formation of solid electrolyte interface (SEI) films on the cathode and anode simultaneously. The alternating current impedance and X-ray diffraction suggest that the SEI films derived from DPDS are helpful for enhancing the interface performance of the electrodes and protecting the Li1.2Mn0.54Ni0.13Co0.13O2 and graphite structures from deterioration during high-temperature cycling, which is responsible for the improvement in the performance of the Li1.2Mn0.54Ni0.13Co0.13O2/graphite batteries at elevated temperature. (C) 2017 Elsevier Ltd. All rights reserved.