Electrochimica Acta, Vol.240, 371-378, 2017
Electrochemical performance of polymer electrolytes based on Poly (vinyl alcohol)/Poly(acrylic acid) blend and Pyrrolidinium ionic liquid for lithium rechargeable batteries
Polymer electrolytes offer the most promising solution to address the all-solid-state battery requirements such as flexibility, leak-proof packing and easy processing. In this study, a polymer blend of 25 mol% poly(acrylic acid) (PAA) and 75 mol% polyvinyl alcohol) (PVA) was optimized based on its thermal, mechanical and structural properties. The ionic liquid (IL) electrolyte, 1-butyl-1-methylpyrrolidinium bis(trifluoromethanesulfonyl)imide (PYRTFSI) with 0.2 m lithium bis(trifluoromethansulfonyl) imide (LiTFSI), was added to the polymer blend in different molar ratios. A maximum ionic conductivity of 1 mS cm(-1) is observed at 90 degrees C in the membrane with 70 mol% IL. Cyclic voltammetry of the polymer electrolytes shows peaks corresponding to lithium stripping (+0.25 V vs. Li+/Li) and deposition (-0.3 V vs. Li+/Li) processes indicating the occurrence of a highly reversible redox process. The electrochemical stability window of these polymer electrolytes, as determined by linear sweep voltammetry, extends up to 5 V, suggesting that these electrolytes could be suitable for batteries that use high voltage cathode materials. A lithium transference number (t(Li+)) of 0.4 was determined for the polymer electrolytes by using chronoamperometry and impedance measurements. Galvanostatic charge-discharge studies of the polymer electrolytes in a lithium half-cell with LiCoO2 (LCO) as cathode delivers a capacity of about 100 mAhg(-1) at 60 degrees C. Coin-type half-cell with LiFePO4 (LFP) cathode and the polymer electrolyte containing 70 mol% IL delivered a capacity of 172 mAhg(-1). Interestingly, the LFP/polymer composite cathode (LFP-C) delivers a higher capacity (215 mAh g(-1) at 60 degrees C) than the pristine LiFePO4 cathode. (C) 2017 Elsevier Ltd. All rights reserved.