Electrochimica Acta, Vol.232, 123-131, 2017
Unravelling the growth mechanism of hierarchically structured Ni-1/3Co1/3Mn1/3(OH)(2) and their application as precursors for high-power cathode materials
A hydroxide co-precipitation method is used to synthesize transition metal hydroxide (Ni1/3Co1/3Mn1/3(OH)(2)), which is the precursor for layer-structured LiNi1/3Co1/3Mn1/3O2. The optimum pH range for the preparation of Ni1/3Co1/3Mn1/3(OH)(2) using a continuous stirred-tank reactor is calculated by taking into account the underlying chemical equilibria. The entire growth process of the Ni1/3Co1/3Mn1/3(OH)(2) particles is investigated by monitoring the structure, morphology, particle size distribution, and tap density as a function of the reaction time. The results confirm that the co-precipitation reaction in the presence of ammonia started with the formation of crystal nuclei and (001) plane dominated nanosheets. The reaction ended with spherical and dense hydroxide precursors. The crystal growth mechanism was interpreted during the co-precipitation process, which involved the quick nucleation of primary particles followed by its slow aggregation and crystallization. The electrochemical properties of the final cathode materials with different morphologies are also studied. The results show that the electrochemical performances of the final LiNi1/3Co1/3Mn1/3O2 are strongly affected by the hierarchical structure of Ni1/3Co1/3Mn1/3(OH)(2). (C) 2017 Elsevier Ltd. All rights reserved.