Applied Surface Science, Vol.391, 184-193, 2017
Enhanced visible light activity on direct contact Z-scheme g-C3N4-TiO2 photocatalyst
Direct contact Z-scheme g-C3N4-TiO2 nanocomposites without an electron mediator are prepared via simple annealing the mixture of bulk g-C3N4 and nanotube titanic acid (NTA) in air at 600 degrees C for 2 h. In the process of annealing, the bulk g-C3N4 transformed to ultra-thin g-C3N4 nanosheets, and NTA converted to a novel anatase TiO2, then the two components formed a close interaction. The XPS result reveals that some amount of nitrogen is doped into this novel-TiO2, and g-C3N4 nanosheets exist in the composites. The results of XRD, TEM and TG indicate that the thickness of g-C3N4 nanosheets is very thin. The ESR spectrum shows the existence of Ti3+ and single-electron-trapped oxygen vacancy in the 30%g-C3N4-TiO2 composites. In photocatalytic activity test, the 30%g-C3N4-TiO2 nanocomposites showed an excellent photo-oxidation activity of propylene under visible light irradiation (lambda >= 420 nm), and the removal efficiency of propylene reached as high as 56.6%, and the activity kept nearly 82% after four consecutive recycles. Photoluminescence (PL) result using terephthalic acid (TA) as a probe molecule indicated that the g-C3N4-TiO2 nanocomposites displayed a Z-sheme photocatalytic reaction system and this should be the main reason for the high photocatalytic activity. A possible photocatalytic mechanism was proposed on the basis of PL result and transient photocurrent-time curves. (C) 2016 Elsevier B.V. All rights reserved.