Journal of Crystal Growth, Vol.451, 194-199, 2016
Quality improvement of CdMnTe:In single crystals by an effective post-growth annealing
In this paper, an effective annealing method in which CdMnTe:In (CMT:In) single crystals were coated with CMT powders of the same composition was used to improve the crystal quality of CMT:In crystals. The results indicated that the density of Te inclusions decreased as the annealing time increased. The resistivity and IR transmittance of annealed CMT:In crystals were enhanced obviously. The resistivity of 120 h annealed crystal increased even two orders of magnitude. The reduction of full-width at-half maximum (FWHM) and the increase of the intensity of X-ray rocking curve indicated an improvement of the crystal quality. PL measurements also showed the crystal quality improved after annealing. No characteristic peak of Am-241 gamma-ray could be observed in the detector fabricated with as-grown crystal. Remarkably, for the detector fabricated with annealed crystals, the peak of Am-241 gamma-ray appeared. And the energy resolution and mu tau value were improved as the annealing time increased. Specially, 120 h annealed CMT:In crystal with 10.11% energy resolution and 1.20 x 10(-3) cm(2)/V mu tau value has the best detector performance. (C) 2016 Elsevier B.V. All rights reserved.