Journal of Membrane Science, Vol.514, 322-331, 2016
Weak polyelectrolyte multilayers as tunable membranes for solvent resistant nanofiltration
This manuscript encompasses the investigation into the solvent resistant nanofiltration (SRNF) performance of multilayer membranes prepared from weak polyelectrolytes. These weak polyelectrolytes are unique in that the charge density is not fixed and depends on the coating pH, adding an extra variable as tuning parameter for SRNF performance. The weak polyelectrolyte based multilayers (PEMs) were prepared on a hydrolyzed PAN support membrane from poly(allylamine hydrochloride) (PAH) as polycation and poly(acrylic acid) (PAA) as polyanion. Detailed investigations on the role of the pH of the coating solution on the performance of the prepared SRNF-membranes were carried out with organic dyes of different size (similar to 300-1000 Da) and charge. Variation in pH of the coating solutions was found to lead to a large degree of control over the separation performance of the prepared SRNF-membranes for the different dyes. The solvent permeabilities and the dye retentions were measured and correlated to variations in the PEM membrane structures, with more dye adsorption being found for membranes with more free acid and amine groups. The membranes were also found to be stable for long termfiltrations in solvents such as isopropyl alcohol (IPA), acetonitrile (ACN), tetrahydrofuran (THF) and in the challenging polar aprotic solvent, N,N-dimethylformamide (DMF). Results of this study clearly demonstrate the potential of using pH as tuning parameter for weak PEMs to prepare SRNF-membranes optimized for specific applications. (C) 2016 Elsevier B.V. All rights reserved.