Solid-State Electronics, Vol.110, 29-34, 2015
Arsenic atomic layer doping in Si using AsH3
Atomic layer doping of arsenic (As-ALD) in Si is investigated using a single wafer reduced pressure chemical vapor deposition tool. Hydrogen-free and hydrogen-terminated Si surfaces are exposed to AsH3 in the temperature range between 300 degrees C and 700 degrees C followed by Si capping using H-2-SiH4 or H-2-Si2H6 gas mixture at 450-700 degrees C. After exposing to AsH3 below 400 degrees C, no As spike formation is observed on both hydrogen-free and hydrogen-terminated Si surface. The incorporated As dose is increasing with increasing AsH3 exposure time and saturates. Before saturation, a higher As dose is observed at higher AsH3 partial pressure for the same AsH3 exposure time. As incorporation is not influenced by the precursor (SiH4 or Si2H6) used for Si buffer deposition. By increasing SiH4 or Si2H6 partial pressure, a higher amount of As is incorporated at AsH3 exposed surface and a higher background doping of segregated As in the Si cap is observed. The slope of the segregated As is not influenced by the growth rate at 600 degrees C, which means that the As segregation seems to be under thermal equilibrium. Lower segregation of As in the Si cap is observed at lower Si cap growth temperature. The results shown here may offer a precise location and dose control of As into Si. (C) 2015 Elsevier Ltd. All rights reserved.