Improved catalytic performance of CaO and CeO2 promoted Ni catalyst on gasifier bed material for tar removal from producer gas
A new catalytic material containing the mixture of Ni, CaO and CeO2 for catalyzing commercial gasifier bed material (Carbo HSP) was synthesized and characterized by XRD, TPR/TPO, TPD and SEM techniques. The catalyst performance for tar removal in simulated producer gas mixture via steam reforming was tested in a lab-scale fix-bed reactor at atmospheric pressure and over a temperature range from 600 to 800 degrees C. The combination of Ni-CaO-CeO2 had significantly higher activity for toluene removal as compared to Ni, Ni-CaO or Ni-CeO2 systems. At 700 degrees C, the optimum composition 2.5 wt.% (Ni20Ca60Ce20) displayed 68% and 52% conversions for C7H8 and C2H4 respectively, leading to the highest CO2 selectivity. This catalyst composition shows only 7% (from 100% to 93%) deactivation in activity after 48 h in time-on-stream at 800 degrees C. After regeneration with an O-2/H-2 sequence, the conversion recovers to 100% and decreased only to 95% after 48 h in time-on-stream. Ni activity and stability are enhanced from the individual roles of CaO and CeO2. The CeO2 can act as redox component that provides for a higher H2O dissociation leading to carbon oxidation and the CaO can enhance the basicity of the catalyst as well as provide for a higher dispersion of Ni metal. The catalytic steam reforming of tars also results in a higher H-2-to-CO ratio. (C) 2015 Elsevier B.V. All rights reserved.