Sol-gel preparation and characterization of SiO2 coated VO2 films with enhanced transmittance and high thermochromic performance
Vanadium dioxide (VO2) films prepared at low-temperature with a low cost are considerable for energy-saving applications. Here, SiO2 coated VO2 films with clearly enhanced visible transmittance by introducing antireflection coatings (ARCs) and excellent thermochromic performance were present. The VO2 films have been prepared via a stable and low-cost sol-gel synthesis route using vanadium pentaoxide powder as precursor, and their structural, morphological, optical and electrical properties and thermochromic performance were systemically characterized. The resistance of VO2 films varies by 4 orders of magnitude and the transmittance changes from 11.8% to 69.3% at 2500 nm while no significant deviation appears in the visible region during metal-insulator transition (MIT). Nanoporous SiO2 coating with good optical transparency was coated on the surface of VO2 film via sol-gel dip-coating technique to enhance its optical transmittance, and the visible transmittance is increased by 14.6% due to the significantly decreased reflectance. The critical transition temperature (63 degrees C) and infrared switching properties of VO2 films are not much deteriorated by applying SiO2 layer. The synergistic effect of antireflection and thermochromism on SiO2 coated VO2 films was investigated. (C) 2014 Elsevier B.V. All rights reserved.