굴패각과 인산으로부터 수산화아파타이트 분말 합성에 관한 연구
A Study on The Synthesis of Hydroxyapatite Powders Using Oyster Shells and H 3 PO 4
E-mail:
Hydroxyapatite powders were prepared after heating at 1250 ? C by the direct reaction using oyster shells and H 3 PO 4 . Properties of hydroxyapatite powders were investigated as XRF, XRD, DTA, FT-IR, SEM. Only hydroxyapatite was observed in XRD powders which was heated at 1250 ? C for 2 hours and there was no remained CaO in that sample. And the results of FT-IR of sample was confirmed hydroxyapatite. Sample was agglomerated together, but needle shape morphology was observed in powders heated at 1250 ? C .
  1. Hench LL, J. Am. Ceram. Soc., 74(7), 1487 (1991)
  2. AKaO M, Ceramics Japan, 20(12), 1096 (1985)
  3. Lee SG, Ko HY, J. Korea. Ceram. Soc., 26(2), 171 (1989)
  4. Jarcho M, Bolen CH, Thomas MB, J. Mater. Sci., 11, 2027 (1976)
  5. Aoki M, Kato K, Ceramics Japan, 107, 469 (1975)
  6. Fowler BO, Inorg Chem., 13(1), 207 (1974)
  7. Shin YG, Jung HJ, Kim BH, J. Korea. Ceram. Soc., 26(2), 157 (1989)
  8. Kim CE, Park H, Kim BY, Lee DY, J. Korea. Ceram. Soc., 27(7), 907 (1990)
  9. Hayek E, Newesely E, Inorganic syntheses Ⅶ/ McGraw-Hill, pp.63-65, 1963 (1963)
  10. Tagai H, Aoki H, Hastings GW, Williams DF, John Wiley&sons 477-488 (1980) (1980)
  11. Blakeslee KC, Condrate RA, Sr., J. Am. Ceram. Soc., 54(11), 559 (1970)
  12. Lee JE, Park H, Kim CE, J. Korea. Ceram. Soc., 33(1), 10 (1996)