3 wt.% Cu 함유 STS 304 빌렛의 열간가공성과 표면결합에 미치는 δ-ferrite의 영향
Effect of δ-Ferrite on the Hot Workability and Surface Defect of STS 304 Billets Containing 3 wt. % Cu
E-mail:
To investigate the effect of D-ferrite on the hot workability and surface defect of STS 304 billets containing 3 wt. % Cu, microstructure observations and high temperature mechanical properties test were carried out for the specimens extracted mainly from raw or oxidized billets. It was found that the total δ -ferrite content has little influence on the hot workability, even though the fracture cracks due to high temperature tension or compression test were initiated and propagated mostly along δ / γ boundary in the specimens. On the other hand, it was supposed that the direct causes of surface defects in the wire rolled from the as-continuously cast billet were the grain boundary embrittlement arose from the deep diffusion of oxygen into the grain boundary, and the oxidation of δ -ferrite connected by a grain boundary to the surface during the billet reheating process as well.
- Choi JY, Jin W, J. Kor. Inst. Met. & Mater., 37(1), 27 (1999)
- Ahn YS, Lee YH, Lee YD, J. Kor. Inst. Met. & Mater., 30(7), 799 (1992)
- Jolley G, Geraghty JE, Solidification & Casting of Metals, The Metal Society, p.411, London (1979) (1979)
- Myllykoski L, Act. Univ. Oul., C26, Metallurg., 61 (1983) (1983)
- Lippold JC, Savage WF, Welding Res. Supplement, 12, 388s (1982)
- Decroix JH, Neveu AM, Castro RJ, The Iron and steel Inst. p.135, London (1968) (1968)
- Uematsu Y, Fujimura T, Hoshino K, Nippon Steel Tech. Rep., 25, 47 (1982)
- Fredriksson H, Metall. Trans., 3A, 2989 (1972)
- Lee YY, Kim SK, J. Kor. Inst. Met. & Mater., 30(9), 1104 (1992)
- Lee YY, Sim SD, J. Kor. Inst. Met. & Mater., 34(5), 596 (1996)
- Jenkins CHM, J. Iron and Steel Inst., 136, 187 (1973)
- Henke RH, Lula RA, J. Metals, 883 (1954)