Macromolecular Research, Vol.22, No.12, 1268-1274, December, 2014
Fabrication and characterization of three-dimensional silk fibroin scaffolds using a mixture of salt/sucrose
E-mail:
This study described the preparation of three-dimensional (3-D) silk fibroin (SF) scaffolds, which derived from a mixed salt/sucrose leaching without the process of lyophilization. Compared with the previous method, this fabrication of 3-D SF scaffold is simple and can have more diverse morphological appearances of pores depending on the different salt/sucrose mixing concentrations. The correlation between pore shape and septum of SF scaffolds or salt concentration was examined by SEM. Additionally, the effects of salt or glucose concentrations on mechanical properties, such as compressive modulus in dry and wet states, were studied. For the materials with ranged between 69?88%, water binding capacity decreased with increasing salt or decreasing sucrose. After cell seeding and culture, SEM images of scaffolds showed that cell infiltrations were increased along with increased sucrose concentration. Analysis of Masson’s trichrome staining showed positive findings for collagen deposits in scaffolds of the 100% sucrose type. Thus, our new method can fabricate 3-D SF scaffolds with different characteristics, and may be used for various tissue engineering uses.
  1. Agrawal CM, Ray RB, J. Biomed. Mater. Res., 55, 141 (2001)
  2. Hollinger JO, Leong K, Biomaterials, 17, 187 (1996)
  3. Hu Y, Grainger DW, Winn SR, Hollinger JO, J. Biomed. Mater. Res., 59, 563 (2002)
  4. Dang JM, Leong KW, Adv. Drug Deliv. Rev., 58, 487 (2006)
  5. Laschke MW, Rucker M, Jensen G, Carvalho C, Mulhaupt R, Gellrich NC, Menger MD, J. Biomed. Mater. Res. A, 85, 397 (2008)
  6. Saul JM, Linnes MP, Ratner BD, Giachelli CM, Pun SH, Biomaterials, 28, 4705 (2007)
  7. Altman GH, Diaz F, Jakuba C, Calabro T, Horan RL, Chen J, Lu H, Richmond J, Kaplan DL, Biomaterials, 24, 401 (2003)
  8. Santin M, Motta A, Freddi G, Cannas M, J. Biomed. Mater. Res., 46, 382 (1999)
  9. Wong C, Foo P, Kaplan DL, Adv. Drug Deliv. Rev., 54, 1131 (2002)
  10. Kim UJ, Park J, Kim HJ, Wada M, Kaplan DL, Biomaterials, 26, 2775 (2005)
  11. Kim HJ, Kim UJ, Vunjak-Novakovic G, Min BH, Kaplan DL, Biomaterials, 27, 4442 (2005)
  12. Wang Y, Blasioli DJ, Kim HJ, Kim HS, Kaplan DL, Biomaterials, 27, 4434 (2006)
  13. Zhang X, Baughman CB, Kaplan DL, Biomaterials, 29, 2217 (2008)
  14. Minoura N, Aiba S, Gotoh Y, Tsukada M, Imai Y, J. Biomed. Mater. Res., 29, 1215 (1995)
  15. Unger RE, Peters K, Wolf M, Motta A, Migliaresi C, Kirkpatrick CJ, Biomaterials, 25, 5137 (2004)
  16. Unger RE, Wolf M, Peters K, Motta A, Migliaresi C, Kirkpatrick CJ, Biomaterials, 25, 1069 (2004)
  17. Gotoh Y, Niimi S, Hayakawa T, Miyashita T, Biomaterials, 25, 1131 (2004)
  18. Chen X, Qi YY, Wang LL, Yin Z, Yin GL, Zou XH, Ouyang HW, Biomaterials, 29, 3683 (2008)
  19. Zhang X, Cao C, Ma X, Li Y, J. Mater. Sci. Mater. Med., 23, 315 (2012)
  20. Yan LP, Oliveira JM, Oliveira AL, Caridade SG, Mano JF, Reis RL, Acta Biomater., 8, 289 (2012)
  21. Wang Y, Bella E, Lee CS, Migliaresi C, Pelcastre L, Schwartz Z, Boyan BD, Motta A, Biomaterials, 31, 4672 (2010)
  22. Zhang R, Ma PX, J. Biomed. Mater. Res., 44, 446 (1999)
  23. Soliman S, Sant S, Nichol JW, Khabiry M, Traversa E, Khademhosseini A, J. Biomed. Mater. Res. A, 96, 566 (2011)
  24. Alcantar NA, Aydil ES, Israelachvili JN, J. Biomed. Mater. Res., 51, 343 (2000)
  25. Desai NP, Hubbell JA, Biomaterials, 12, 144 (1991)
  26. Kim UJ, Park JY, Li CM, Jin HJ, Valluzzi R, Kaplan DL, Biomacromolecules, 5(3), 786 (2004)