Korean Journal of Materials Research, Vol.22, No.11, 626-630, November, 2012
전사지를 이용 적층한 셀 구조 및 연료극 기능층 형성에 따른 출력 특성
Power Densities According to Anode Functional Layers on the Manufactured SOFC Unit Cells Using Decalcomania Method
E-mail:
The properties of SOFC unit cells manufactured using the decalcomania method were investigated. SOFC unit cell manufacturing using the decalcomania method is a very simple process. In order to minimize the ohmic loss of flattened tube type anode supports of solid oxide fuel cells(SOFC), the cells were fabricated by producing an anode function layer, YSZ electrolyte, LSM electrode, etc., on the supports and laminating them. The influence of these materials on the power output characteristics was studied when laminating the components and laminating the anode function layer between the anode and the electrolyte to improve the output characteristics. Regarding the performance of the SOFC unit cell, the output was 246 mW/ cm2 at a temperature of 800oC in the case of not laminating the anode function layer; however, this value was improved by a factor of two to 574 mW/cm2 due to the decrease of the ohmic resistance and polarization resistance of the cell in the case of laminating the anode function layer. The outputs appeared to be as high as 574 and 246 mW/cm2 at a temperature of 800oC in the case of using decalcomania paper when laminating the electrolyte layer using the in dip-coating method; however, the reason for this is that interfacial adhesion was improved due to the dense structure, which leads to a thin thickness of the electrolyte layer.
  1. Park ST, Choi BH, Ji MJ, An YT, Choi HJ, J. Kor. Ceram. Soc., 48, 246 (2011)
  2. Singhal SC, Solid State Ion., 152, 405 (2002)
  3. Tompsett GA, Finnerty C, Kendall K, Alston T, Sammes NM, J. Power Sources, 86, 376 (2000)
  4. Fukui T, Murata K, Ohara S, Abe H, Naito M, Nogi K, J. Power Sources, 125(1), 17 (2004)
  5. Lee YK, Lee YK, Korean J. Mater. Res., 22(9), 470 (2012)
  6. Kim SD, Hyun SH, Moon J, Kim JH, Song RH, J. Power Sources, 139(1-2), 67 (2005)
  7. Reitz TL, Xiao HM, J. Power Sources, 161(1), 437 (2006)
  8. Von Dollen P, Barnett S, J. Am. Ceram. Soc., 88(12), 3361 (2005)
  9. Chen KF, Chen XJ, Lu Z, Ai N, Huang XQ, Su WH, Electrochim. Acta, 53(27), 7825 (2008)
  10. Lee MJ, Kim BN, Lim TY, Kim SK, Choi BH, J. Kor. Ceram. Soc., 48, 520 (2011)
  11. Ai N, Lu Z, Chen KF, Huang XQ, Wei B, Zhang YH, Li SY, Xin XS, Sha XQ, Su WH, J. Power Sources, 159(1), 637 (2006)
  12. Cho NU, Hwang SC, Lee IS, J. Kor. Ceram. Soc., 44, 720 (2007)
  13. Herle JV, Ihringer R, Cavieres RV, Constantin L, Bucheli O, J. Eur. Ceram. Soc., 21, 1855 (2001)