Experimental research on grind-hardening of 65Mn steel
Grind-hardening was done on 65Mn steel with a conventional surface grinder and a corundum-grinding wheel. Research was conducted to probe into microstructures and properties of the hardened layer under varied depth of cut and cooling conditions. Results show that the hardened layer does not change noticeably in their martensitic structures and micro-hardness, which is ranged between 810-870HV. When the depth of cut increases or the dry grinding technique is adopted, the hardened layer becomes thicker accordingly. Under the condition of dry grinding with the depth of cut 1.0mm, the hardened layer depth reaches 2.0mm. It can find applications in grinding and metal surface modification field.