Materials Science Forum, Vol.486-487, 354-357, 2005
The effect of defect locations on the stress distribution and crack initiation in monolithic aluminum vs. GLARE hybrid composite
This paper investigates the effect of the defect location on the stress concentration, the stress distribution, and the crack initiation behavior when the defects were made in the vicinity of the circular hole in the monolithic aluminum and the glass fiber reinforced laminates (GLARE). As the defect location in the vicinity of the circular hole was changed from theta(4) = 90 degrees to theta(1) = 0 degrees, the stress concentration was increased. Generally, the stress concentration of GLARE was about 15% greater than that of the monolithic aluminum. When the defect was at theta(2) = 30 degrees Multi Site Damage (MSD) crack was found in the monolithic aluminum, but just the main cracks existed in GLARE. The delamination. instead of MSD crack was made in GLARE, and it resulted in the prevention against the second crack initiation.