Composite ionic liquid and polymer membranes for gas separation at elevated temperatures
In recent years, the utilization of ionic liquids supported on porous polymer membranes has been demonstrated to enhance gas separation performance by improving both permeability and selectivity for several industrially-relevant gas mixtures. However, the use of such supported ionic liquid membranes (SILMs) is normally not feasible at elevated process temperatures due to the resulting decrease in ionic liquid viscosity, which can lead to increased loss of ionic liquid from the membrane support during operation. In addition, many of the polymer membranes typically used in SILMs exhibit relatively poor mechanical and thermal stabilities at high temperatures. To overcome these problems associated with SILMs, thermally-stable composite ionic liquid and polymer membranes (CILPMs) have been fabricated in this study, thus exploiting the beneficial properties of ionic liquids for gas separation at elevated temperatures. Poly(pyromellitimide-co-4,4'-oxydianiline) (PMDA-ODA PI) and polybenzimidazole (PM) in combination with the ionic liquid, [C(4)mim][NTf2] were used to fabricate the CILPMs. A measurement rig was designed and built to determine permeabilities and selectivities of the CILPMs for H-2, N-2, CO, CO2 and CH4 over a range of pressures and temperatures. The fabricated CILPMs were shown to maintain excellent mechanical and thermal stability over a wide range of processing conditions. Temperature was shown to greatly affect both permeability and selectivity of the membranes, whilst pressure had less influence, The incorporation of [C(4)mim][NTf2] into the membranes was found to significantly increase CO2 permeation and, therefore, it is anticipated that these CILPMs hold significant potential for CO2 separation applications. (C) 2013 Elsevier B.V. All rights reserved.