Electrochimica Acta, Vol.130, 76-81, 2014
Dye-sensitized solar cells based on electrospun polyacrylonitrile (PAN) nanofibre membrane gel electrolyte
Dye Sensitized Solar Cells (DSSCs) based on electrospun nanofibre membrane electrolytes offer several advantages over liquid electrolyte based solar cells. Nanofibre membranes having different thicknesses were prepared by electrospinning on platinum electrodes from a 11 wt% solution of polyacrylonitrile (PAN) in N,N-dimethylformamide (DMF) at an applied voltage of 8 kV. The membranes were then activated by immersing in a solution containing potassium iodide (KI) (0.06g), propylene carbonate (PC) (0.8g) and iodine (I-2) (0.0092 g) for 30 minutes to obtain "gel" type membrane electrolytes with different thicknesses. These nanofibre membrane electrolytes were used to fabricate quasi-solid state (gel) DSSCs and the performance of these solar cells were compared with DSSCs fabricated with liquid electrolyte (KI:PC:I-2) and conventional PAN based gel electrolyte (PAN:KI:PC:I-2). DSSC with nanofibre membrane electrolyte of thickness 9.14 mu m showed the highest light-to-electricity conversion efficiency of 5.2% whereas an identical cell based on corresponding liquid electrolyte showed an efficiency of 5.3%. The open circuit voltage (V-oc), short circuit current density (J(sc)) and fill factor for the solar cell based on this electrolyte was 0.67V, 13.31 mA cm(-2) and 59% respectively at an incident light intensity of 1000W m(-2) with a 1.5 AM filter. (C) 2014 Elsevier Ltd. All rights reserved.