Quasi-epitaxial barium hexaferrite thin films prepared by a topotactic reactive diffusion process
Quasi-epitaxial barium hexaferrite thin films (BaM) with crystallographic c-axis parallel to film normal were prepared through a topotactic reactive diffusion process using two-step solution deposition on c-plane sapphire. The two-step spin coating process involves preparing an epitaxial hematite film, coating the film with barium precursor solution and thermal annealing. The crystal orientation and magnetic anisotropy of BaM thin films were investigated by X-ray diffraction analysis, SEM observation and magnetic measurements. Hysteresis loops showed good magnetic anisotropy and high remanence ratio (RR) Mr/Ms = 0.97. The films fabricated by two-step spin coating process displayed wider rocking curve width but better magnetic anisotropy than one-step spin coating. The possible mechanism of this discrepancy is discussed in this paper. (C) 2013 Elsevier B.V. All rights reserved.