화학공학소재연구정보센터
Journal of Adhesion, Vol.76, No.4, 307-334, 2001
Surface energy and adhesion studies on acrylic pressure sensitive adhesives
The surface energy and adhesion dynamics of pressure sensitive adhesives-like networks (PSA-LNs) as mimics for PSAs were studied using JKR-based contact mechanics and peel tests. Acrylic acid (AA) was co-polymerized with 2-ethyl hexyl acrylate (2-EHA) and 1,6-hexane diol diacrylate (HDDA) to create PSA-LNs. The measured surface energy (27 to 31 mJ/m(2)) was sensible as surmised from their structure. Acrylic acid content increases the surface energy, threshold adhesion energy and adhesion hysteresis of PSA-LNs. Measurements of adhesion dynamics showed a dependence of adhesion energy to the 0.6-0.8 power of crack speed, depending upon the model chosen for analysis of the data. When compared with actual pressure-sensitive adhesive tape peel tests, the adhesion dynamics data predicted the peel strength. This study shows a direct relationship between threshold adhesion energy, crack propagation mechanics and peel strength measurements.