Volume 25, Issue 10, October 1984, Pages 1527-1533
Polymer

Polymer paper
Rubber phase dispersion in polypropylene

https://doi.org/10.1016/0032-3861(84)90121-6Get rights and content

Abstract

Impact properties of rubber-modified blends are significantly dependent on particle size and size distribution (dispersion). Past work has shown strong variations in these particle parameters with different processing conditions and these variations reflect, in part, different shear fields developed during melt extrusion and moulding. A major problem ensues involving property variability because of process variability. It is neither practical nor economical to place stringent controls on process variability in a plant. Instead, our current research has indicated that lightly crosslinking the rubber reduced drastically the sensitivity of dispersion to processing conditions, and, with the correct rheology between the rubber and the resin, the same dispersion could be maintained through both the extrusion and moulding stages resulting in finished parts with increased chance of dispersion and property consistency. Four rubbers of different degrees of crosslinking and three polypropylenes of different melt flow and structure were blended at six rubber levels. Mixing was carried out with two twin-screw configurations and the blends were cast or injection moulded using a ram or a screw moulder representing six different processing shear histories. Dispersion was quantitatively characterized by scanning electron microscopy (SEM). Spherical rubber particles revealed on the fracture surface were counted and measured to determine particle size and size distribution for the individual blends. Correlation of the results indicated how particle size and size distribution was influenced by crosslinking and the rubber/resin rheology. This provided some understanding of the mechanics of soft-phase dispersion in these blends.

References (12)

  • S. Danesi et al.

    Polymer

    (1978)
  • D. Heikens et al.

    Polymer

    (1977)
  • M. Baer

    J. Appl Polym. Sci.

    (1972)
  • C.G. Bragaw

    Advances in Chemistry

  • W.M. Speri et al.

    Polym. Eng. Sci.

    (1975)
  • C.K. Riew et al.

    Advances in Chemistry

    (1976)
There are more references available in the full text version of this article.

Cited by (88)

  • Design of high impact thermal plastic polymer composites with balanced toughness and rigidity: Toughening with one phase modifier

    2019, Polymer
    Citation Excerpt :

    Here, it should be mentioned that extremely small particle cannot act as an effective impact modifier [39,56]. It is considered that there is an optimal size for rubber or elastomer modifier, and the optimal size is 0.5 μm for the PP/rubber blends [57,58]. From Fig. 6, it is seen that the PP composites modulus is markedly lower than that of PETG composites and nylon composites.

  • Ternary blends based on poly (ethylene-naphthalate)/glass fibers/nitrile rubber: Preparation, properties and effect of dynamic vulcanization

    2013, Polymer Testing
    Citation Excerpt :

    This may be one of the reasons for the large decrease in mechanical properties of the PEN/GF/NBR blends. Typically in the literature, low concentrations of dispersed rubber phase in a continuous plastic phase, e.g. PP/EPDM, are considered to be composed of spherical droplets dispersed in the PP matrix [18,19]. However, in the present PEN/GF/NBE system, the spherical morphology changes to a somewhat elongated pattern with further break-up into smaller spherical particles, resulting in a heterogeneous size distribution of dispersed NBR domains.

  • Preparation, structure and properties of dynamically vulcanized polypropylene/acrylonitrile butadiene rubber/zinc dimethacrylate ternary blend composites containing maleic anhydride grafted polypropylene

    2013, Polymer Testing
    Citation Excerpt :

    Because the PP and non-crosslinked NBR phase were removed by xylene, the particles left are the crosslinked NBR phase. Typically in the literature, low concentrations of dispersed rubber in PP blends are considered to be composed of spherical droplets dispersed in the PP matrix [18]. However, as shown in Fig. 6a, the irregular shapes of crosslinked rubber particles are observed in the composite without MA-g-PP (80/20-2-0).

  • PP/EPDM-based dynamically vulcanized thermoplastic olefin with zinc dimethacrylate: Preparation, rheology, morphology, crystallization and mechanical properties

    2012, Polymer Testing
    Citation Excerpt :

    The samples etched by boiling xylene are shown in Fig. 7. Typically in the literature, low concentrations of dispersed EPDM in PP blends are considered to be composed of spherical droplets dispersed in the PP matrix [24,25]. The spherical crosslinked rubber particles can be observed in T80/20 (Fig. 7(a)).

View all citing articles on Scopus
View full text