Application of Spray Pyrolysis Process for the Preparation of Nano Sized Cobalt Oxide Powder
E-mail:
In this study, nano-sized cobalt oxide powder with an average particle size below 50 nm was prepared from a cobalt chloride solution by the spray pyrolysis process. The influences of reaction temperature on the properties of the generated powder were examined. The average particle size of the particles formed based on the spray pyrolysis process at a reaction temperature of 700 oC is roughly 20 nm. Moreover, most of these particles cannot appear with an independent type, thereby coexisting in a droplet type. When the reaction temperature increases to 800 oC, the average particle size not only increases to roughly 40 nm but also shows a more dense structure while the ratio of particles which shows a polygonal form significantly increases. As the reaction temperature increases to 900 oC, the distribution of the particles is from roughly 70 nm to 100 nm, while most of the particle surface is more intricately close and forms a polygonal shape. When the reaction temperature increases to 1000 oC, the particle size distribution of the powder shows an existing form from 80 nm to at least 150 nm in an uneven form. As the reaction temperature increases, the XRD peak intensity gradually increases, yet the specific surface area gradually decreases.
  1. Nakamura T, Okano Y, Proceeding of the ICF, C1-101, 7 (1996)
  2. Udawatte CP, Yanagisawa K, J. Am. Ceram. Soc., 84(1), 251 (2001)
  3. Yu J, Kim D, Korean J. Mater. Res., 23(2), 81 (2013)
  4. Yu JK, Kim DH, Powder Tech., 235(2), 1030 (2013)
  5. Yu JK, Kim DH, J. of Nanosci. Nanotechnol., 12(2), 1545 (2012)
  6. Yu JK, Kim DH, J. Ceram. Soc. Jpn., 117(10), 1078 (2009)
  7. Yu JK, Kang SG, Chung KC, Han JS, Kim DH, Mater. Trans., 48(2), 249 (2007)
  8. Yu JK, Kang SG, Kim JB, Kim JY, Han JS, Yoo JW, Lee SW, Ahn ZS, Mater. Trans., 47(7), 1838 (2006)
  9. Yu JK, Kim KW, Kim TS, Kim JY, Mater. Trans., 46(7), 1695 (2005)
  10. Majumdar D, Shefelbine TA, Kodas TT, J. Mater. Res., 11(11), 2861 (1996)
  11. Pluym TC, Kodas TT, J. Mater. Res., 10(7), 1661 (1995)
  12. Messing GL, Zhang SC, Jayanthi GV, J. Am. Ceram. Soc., 76(11), 2707 (1993)
  13. Barin I, Thermochemical Data of Pure Substances, VCH, Germany, 1392-1404. (1989)